- Binary alloys Cu - Sn -Zn -Pb (Low content Pb)
| Binary alloys Cu - Sn -Zn -Pb (Low content Pb) - Correspondent alloys in foreign unification |
| Designation |
|
Standard |
|
ASTM B 505 |
|
BS 1400 |
|
|
DIN 1705 |
|
ISO 1338 |
| BZN2 |
|
UNI 1698 |
|
- - - - |
|
- - - - |
|
|
- - - - |
|
- - - - |
| BZN6 |
|
UNI 1698 |
|
923 |
|
- - - - |
|
|
- - - - |
|
- - - - |
| Lega G |
|
RIV |
|
922 |
|
LG4 |
|
|
- - - - |
|
- - - - |
| 90/10 Ind. |
|
Tonolli |
|
- - - - |
|
- - - - |
|
|
- - - - |
|
Cu Sn Pb2 |
| Lega C |
|
FIAT |
|
927 |
|
- - - - |
|
|
- - - - |
|
- - - - |
| Sn 12 Ni1,5 Ind. |
|
Tonolli |
|
- - - - |
|
- - - - |
|
|
- - - - |
|
- - - - |
| 86/14 Ind. |
|
Tonolli |
|
- - - - |
|
- - - - |
|
|
- - - - |
|
- - - - |
| |
|
|
|
|
|
|
|
|
|
|
|
| PERCENTUAL CHEMICAL COMPOSITION |
| Designation |
Cu |
Sn |
Pb max. |
Zn |
Ni |
Fe max. |
Sb max. |
S max. |
P max. |
Mn max. |
More specifications |
| BZN2 |
92-94 |
3-5 |
≤2 |
BAL |
≤1 |
0,2 |
0,1 |
- - - - |
0,05 |
- - - - |
Cu+Sn≥97 |
| BZN6 |
85,5-87,5 |
7,5-8,5 |
≤2,5 |
BAL |
≤1 |
0,2 |
0,3 |
- - - - |
0,05 |
- - - - |
Cu+Sn≥92 |
| Lega G |
BAL |
7-8 |
3-4 |
3-4 |
≤0,5 |
0,3 |
0,3 |
- - - - |
0,05 |
- - - - |
Sb+Fe+P≤0,6 |
| 90/10 Ind. |
85-87 |
7,5-8 |
2-3 |
2,5-3,5 |
≤0,5 |
0,3 |
0,3 |
- - - - |
0,05 |
- - - - |
Sb+Fe+P≤0,6 |
| Lega C |
85-88 |
9-11 |
1-3 |
1-3 |
<0,3 |
0,3 |
0,2 |
0,1 |
0,20 |
0,20 |
Fe+Ni+Sb+ P+S+Mn≤1 |
| Sn 12 Ni1,5 Ind. |
79-81 |
11,5-12,5 |
3-4 |
3-4 |
1,3-1,6 |
0,3 |
0,3 |
- - - - |
0,10 |
- - - - |
Sb+Fe+P≤0,6 |
| 86/14 Ind. |
BAL |
11-12 |
3-3,6 |
3-4 |
≤0,5 |
0,25 |
0,35 |
- - - - |
0,05 |
- - - - |
Sb+Fe+P≤0,6 |